Overview
![](https://www.bullseyeglass.com/wp-content/uploads/pulsing-gradient-striker-icon.gif)
Striker
This style may not reveal (strike to) its target color until fired.
Reactive Potential
Contains: Sulfur (S) / Selenium (Se)
May React With: Copper (Cu), Lead (Pb), and Silver (Ag)
Forms of Glass
Sheet Glass (-0030, -0050), Frit (-0001, -0002, -0003, -0008) Rod (-0576), Stringer (-0107), Ribbon (-0401), and Confetti (-0004)
Detailed Information
About 000125 Sheet Glass
![000125-0050](https://www.bullseyeglass.com/wp-content/uploads/000125-0050-F_03.jpg)
![000125-0030](https://www.bullseyeglass.com/wp-content/uploads/000125-0030-F_03.jpg)
Cold Characteristics
Color variations common from yellow-orange to red-orange. Some slight streaking is common.
![Orange Opal, 000125-0030-F](https://www.bullseyeglass.com/wp-content/uploads/000125-0030-F.jpg)
Working Notes
Cadmium/selenium glass. Can fuse darker (more red) or lighter (more yellow) than cold sheet.
This style is not suitable for kilncasting because it can become incompatible when held at high temperatures for an extended period. It may also become incompatible in instances where processes exceed the parameters of the test for compatibility. Testing recommended when heatwork exceeds these parameters.
About 000125 Frit
![000125-0002](https://www.bullseyeglass.com/wp-content/uploads/000125-0002-F_02.jpg)
![000125-0003](https://www.bullseyeglass.com/wp-content/uploads/000125-0003-F_01.jpg)
![000125-0002](https://www.bullseyeglass.com/wp-content/uploads/000125-0002-F_01.jpg)
![000125-0001](https://www.bullseyeglass.com/wp-content/uploads/000125-0001-F_01.jpg)
![000125-0008](https://www.bullseyeglass.com/wp-content/uploads/000125-0008-F_01.jpg)
Working Notes
This style is not suitable for kilncasting because it can become incompatible when held at high temperatures for an extended period. It may also become incompatible in instances where processes exceed the parameters of the test for compatibility. Testing recommended when heatwork exceeds these parameters.
About 000125 Rod
![000125-0576](https://www.bullseyeglass.com/wp-content/uploads/000125-0576-F_01.jpg)
Cold Characteristics
Opaque.
Working Notes
Torch: Lighter color and greater opacity than in sheet glass form. Keep it bright orange by working with a neutral to oxidizing flame atmosphere. Can turn gray in reduction.
Kiln: Lighter color and greater opacity than in sheet glass form.
This style is not suitable for kilncasting because it can become incompatible when held at high temperatures for an extended period. It may also become incompatible in instances where processes exceed the parameters of the test for compatibility. Testing recommended when heatwork exceeds these parameters.
About 000125 Stringer
![000125-0272](https://www.bullseyeglass.com/wp-content/uploads/000125-0272-F_01.jpg)
![000125-0107](https://www.bullseyeglass.com/wp-content/uploads/000125-0107-F_01.jpg)
![000125-0507](https://www.bullseyeglass.com/wp-content/uploads/000125-0507-F_01.jpg)
Working Notes
This style is not suitable for kilncasting because it can become incompatible when held at high temperatures for an extended period. It may also become incompatible in instances where processes exceed the parameters of the test for compatibility. Testing recommended when heatwork exceeds these parameters.
About 000125 Ribbon
![000125-0401](https://www.bullseyeglass.com/wp-content/uploads/000125-0401-F_01.jpg)
Working Notes
This style is not suitable for kilncasting because it can become incompatible when held at high temperatures for an extended period. It may also become incompatible in instances where processes exceed the parameters of the test for compatibility. Testing recommended when heatwork exceeds these parameters.
About 000125 Confetti
![000125-0004](https://www.bullseyeglass.com/wp-content/uploads/000125-0004-F_01.jpg)
Working Notes
This style is not suitable for kilncasting because it can become incompatible when held at high temperatures for an extended period. It may also become incompatible in instances where processes exceed the parameters of the test for compatibility. Testing recommended when heatwork exceeds these parameters.